The 6061 aluminum sheet for sale in current market has excellent mechanical performances, with an maximum tensile strength of 205MPa and above, yielding strength 55.2MPa, flexibility 68.9GPa, maximum bending resistance 228MPa and bending yielding strength 103 MPa.
1, T1
6061 t1 aluminum is cooled by a high temperature molding process and then naturally aged to a substantially stable state. Applicable to products that are cooled after the high temperature forming process and are not subjected to cold working (straightening and leveling, but without affecting the mechanical properties).
2, T2
6061 t2 aluminum sheet is cooled by a high-temperature molding process and naturally aged to a substantially stable state after cold working. It is suitable for products that are cooled by high temperature molding process, cold worked, or straightened and leveled to increase strength.
3, T3
After solution heat treatment, cold working is performed, and then, natural aging to a substantially stable state. 6061 t3 aluminum for sale is suitable for products that are cold worked, or straightened and leveled to improve strength after solution heat treatment.
4, T4
After solution heat treatment, it is naturally aged to a substantially stable state. Applicable to the solution after solid solution heat treatment, no cold work (straightening, leveling, but not affecting the mechanical properties limit), and then natural aging.
5, T5
6061 t5 aluminum is cooled by a high temperature molding process and then subjected to an artificial aging state. It is suitable for products that are cooled by high-temperature molding process without cold working (straightening and leveling, but without affecting the mechanical properties limit), and then artificially aged.
6. T6
6061 t6 aluminum sheet is the most widely searched temper of 6061. T6 is a state of artificial aging after solution heat treatment, applicable to products that are not subjected to cold working after solution heat treatment (straightening and leveling, but not affecting the limit of mechanical properties).
6.T651
6061-T651 is a high-quality aluminum alloy produced by heat treatment pre-stretching process. Its strength is not comparable to that of 2XXX series or 7XXX series, but its magnesium and silicon alloys have many characteristics, and it has excellent processing properties and excellent welding characteristics. It has excellent characteristics such as electroplating property, good corrosion resistance, high toughness and no deformation after processing, compact and defect-free materials, easy polishing, easy filming and excellent oxidation.
Reprinted from
http://haomei-aluminium.com/en/News/Know...mpers.html