Different industries and production process have different requirements for aluminum sheet in mechanical property, so it will require
aluminum sheet manufacturers to have strengthening treatment in the process of production of
aluminum sheet. At present, there are two mainstream methods to strengthen
aluminum sheet in aluminum industry: it is strengthening in product process and solid-solution to strengthen the aluminum sheet.
How to Strengthen the
Aluminum Sheet
1. Strengthening in
Aluminum Sheet Processing
Strengthening in product process is also called the cold hardening, it is means
aluminum sheet below the recrystallization temperature and experience cold deformation processing such as forging, rolling, drawing, or stretching. When process in cold deformation, aluminum sheet’s internal dislocation density will be increase, and entangled with each other and form the cellular structure, which will hinder dislocation motion. The greater the degree of deformation dislocation tangles, the greater the deformation resistance, the higher the strength will increase. After the cold deformation, the degree of strengthening is different according to different deformation degree, deformation temperature and the properties of the material itself. Cold deformation under the same material at the same temperature, the higher the degree of deformation, the greater the strength, but plasticity is lower.
2. Solid-solution to Strengthen the Aluminum Sheet.
Add some alloy elementS in the pure aluminum to form an infinite solid solution or limited solid solution, which not only can obtain high strength, but also can obtain excellent plasticity and good pressure processing performance. In generally, the most commonly used alloying elements in aluminum solid solution strengthening are copper, magnesium, manganese, zinc, silicon, nickel and other elements.
aluminum sheets are generally formed limited solid solution formation, such as Al-Cu,Al-Mg,Al-Zn,Al-Si,Al-Mn snd other binary alloy formation of solid solution, and they all have larger limit for solubility which can have effect of larger solid solution strengthening.
Strengthening
aluminum sheet, the strength performance will be improved obviously , but its hardness could not have been promoted again; When reach the maximum hardness, no matter what method, it cannot continue to improve the hardness of aluminum sheet, and it has to choose other temper with higher base hardness..