Step 1
Slide on a pair or leather work gloves, safety glasses and a dust mask to protect your skin, eyes and lungs.
VIDEO OF THE DAY
Step 2
Place your aluminum sheet onto a work surface. Fit an appropriate tip -- between size "000" or "2" -- to an oxy-acetylene torch. Ignite the torch.
Step 3
Heat up a quarter-sized spot on the aluminum sheet. Hold the torch flame just off the surface for 30 seconds. Turn off the torch.
Step 4
Touch the tip of a prefabricated 550-degree crayon to the hot spot at a 45-degree angle. Hold it for 10 seconds. Repeat steps 4 and 5 as often as necessary until the crayon turns orange. The 550-degree prefabricated crayon is designed to specifically correspond with the shrink temperature of aluminum. While not 550 degrees itself, the crayon will change colors once the tip reaches 550 degrees.
Step 5
Hammer the aluminum with short, rapid strokes around the hot spot as soon as the shrink temperature is reached. Continue for 15 to 30 seconds. Avoid striking the hot spot directly to prevent additional thinning.
Slide on a pair or leather work gloves, safety glasses and a dust mask to protect your skin, eyes and lungs.
VIDEO OF THE DAY
Step 2
Place your aluminum sheet onto a work surface. Fit an appropriate tip -- between size "000" or "2" -- to an oxy-acetylene torch. Ignite the torch.
Step 3
Heat up a quarter-sized spot on the aluminum sheet. Hold the torch flame just off the surface for 30 seconds. Turn off the torch.
Step 4
Touch the tip of a prefabricated 550-degree crayon to the hot spot at a 45-degree angle. Hold it for 10 seconds. Repeat steps 4 and 5 as often as necessary until the crayon turns orange. The 550-degree prefabricated crayon is designed to specifically correspond with the shrink temperature of aluminum. While not 550 degrees itself, the crayon will change colors once the tip reaches 550 degrees.
Step 5
Hammer the aluminum with short, rapid strokes around the hot spot as soon as the shrink temperature is reached. Continue for 15 to 30 seconds. Avoid striking the hot spot directly to prevent additional thinning.